PLAMCOR®-2 - intumescent fireproof composition

Fire protection of metal structures inside closed heated industrial, civil and public buildings and structures operated in macroclimatic regions UHL and KHL, atmosphere types I and II according to GOST 15150.

PLAMCOR-2 is applied as an intermediate or finish layer in PLAMCOR coating systems for corrosion and fire protection of structural steel. It is recommended to use with ZINEP, ISOLEP-primer, 

ISOLEP-mastic, VINICOR-061, VINICOR-ecoprime-01 and GF-021 (ГФ-021).

If there are special requirements for decorative properties, the PLAMCOR-2 coating should be covered with finishing enamels POLYTON-UR (UV), POLYTON-HV, VINIKOR-62 and other enamels on polyurethane, vinyl-epoxy, vinyl, vinyl chloride, alkyd and other bases.

Fire protection efficiency

Use of other paint products in the protective coating systems is allowed only if approved by the VMP Holding. 

The fire resistance of the loss of bearing capacity:

• with reduced metal thickness 3.4 mm and the thickness of coating 0.8 mm – 45 minutes;

• with reduced metal thickness 3.4 mm and the thickness of coating 1.25 mm – 60 minutes;

• with reduced metal thickness 5.8 mm and the thickness of coating 1.5 mm – 90 minutes;

• with reduced metal thickness 7.2 mm and the thickness of coating 2.1 mm – 120 minutes.

Certification

State registration certificate № RU.66.01.40.015.E.000016.02.14 dated 07.02.2014. 

Certificates of conformity No. EAES RU C-KZ.HE46.V.00011/23 dated 20.10.2023, No. EAES RU C-KZ.HE97.B.00012/24 dated 08.04.2024, No. NSOPB.RU.EO.PR009.N.00258 from 16.08.2023.

Technical data

Coat

Composition

Consumption

Theoretical spreading rate for one-layer coat of thickness 400-800 µm 540-1080 g/m²

Coating service life

Fire retardant coating PLAMKOR-2 as part of a complex coating with a primer and top enamel has a service life of at least 25 years when used in premises of accommodation category 4 according to GOST 15150.

The coating retains its fire retardant efficiency for the specified period in the absence of mechanical damage and constant moisture condensation. After the end of the specified period, the fire retardant coating must be replaced with the complete removal of the existing layer and its subsequent restoration.

Application

The composition of PLAMKOR-2 should be coat to the primer (ZINEP, ISOLEP-primer, ISOLEP-mastic, VINICOR-061, VINICOR-ecoprime-01) not earlier than 24 hours, on GF-021 (ГФ-021) coating – not earlier than 7 days after its application at temperature (20±2)°C (otherwise sagging or cracking of PLAMCOR-2 may occur).

PLAMCOR-2 may be applied at the temperature from minus 25 °С to plus 40 °С and up to 80 % RH (if temperature is lower contact VMP for advice).

The coating is not waterproof. When it is applied and exploit avoid influence of moisture, condensate and other source of water.

Preparation for use:

• mix up thoroughly to homogeneous state with mixer;

• add recommended thinner to achieve workable consistency if it is necessary before the application.

Storage and handling

The composition is packed in tin cans or jars.

Store in dry, shaded conditions away from sources of heat, moisture and ignition, at the temperature from minus 40 to plus 40 °С; GOST 9980.5-2009. The composition must be stored in a hermetically sealed container of the manufacturer away from heat sources. Packaging with the composition should not be exposed to atmospheric precipitation and direct sunlight.

Guaranteed shelf life in the manufacturer’s package units is 24 months from the date of packaging.

Precautions

When working with the enamel one shall observe the existing sectoral standard norms and requirements and safety measures as specified on the package label.

One shall use personal protective equipment (goggles, face masks and respirators) and avoid inhalation of solvents and contact of the substances with skin, eye mucosa, respiratory channels; use inside the premises is allowed only if sufficient ventilation is provided.

The composition is classified as a fire-hazardous material

The information is of general character, without consideration to the object specific nature. Use of materials for other purposes not specified here or in case other influencing factors are present shall be approved by the VMP Holding CJSC in writing. In case of absence of such approval the manufacturer is not held liable for the improper use of the material and the buyer falls from the right to present claims connected with the coating quality..